ASTM A276 and ASTM A479 Titanium Round Bar Weight, Dimensions Chart in mm, kg, PDF online
Titanium round bar is a type of titanium product that is made into a round rod shape that has a circular
cross-section. It is manufactured by hot or cold rolling titanium billets or ingots. Titanium round bars
can be manufactured from different grades and alloys of titanium. The selection of grade depends on the
specific requirements of the application, such as temperature, pressure, and the type of load it will
bear. Common titanium alloys used for round bars include Grade 2, Grade 5 (Ti-6Al-4V), Grade 7, and
Grade 23 (Ti-6Al-4V ELI), among others. All these grades are specified futher in titanium round bar
weight and dimensions chart PDF.
Titanium round bars are corrosion-proof and rust-free, which makes them suitable for use in huge
factories dealing with chemicals. Titanium round bar is also known for its excellent strength, and
ductility. It is also lightweight and has a low coefficient of thermal expansion. These properties make
it an ideal material for applications where high performance and reliability are essential.
Additionally, they have important properties like good weldability, biocompatibility and non-magnetic
nature. These round bars have broad industrial applications, including
those that involve chemical processing and/or high-saline environments. Titanium round bars are
used in a different machinery, mechanisms, valves, fittings, vessels, flanges, threading bars, aerospace
components,
chemical and fuel tankers, marine hardware, escalators, elevators, medical implants, and petrochemicals.
Titanium round bar is also used in a variety of consumer products, such as sporting goods, jewelry, and
watches. Different applications require different standards and grades. All this information is provided
in the weight and dimensions chart PDF on this page. It is important because you have to use it
efficiently for your project needs.
Titanium round bar is a versatile and reliable material that can be used in a wide range of applications:
- Aerospace and defense
- Laboratory Benches and Equipment
- Medical and dental devices
- Oil and gas
- Chemical containers, including for transport
- Marine and offshore
- Power generation
- Food and beverage processing
- Semiconductor manufacturing
- Pharmaceutical manufacturing
- Sporting goods
Titanium Bar Specifications
Titanium Bar Length |
2 to 6 meters or 8 to 20 feet |
Titanium Rod Chamfering |
Available in 30, 45 & 60 degree thru fully automatic both-end chamfering machine
|
Ultrasonic Test of ASTM A276 Threaded Rod |
As per ASTM A-388, EN 10308 (class 1 to 4), API 6A/ISO it is 100% tested thru Digital
Ultrasonic Flaw Detector, 10423:2003-PSL 3, MIL STD 2154, SEP 1920:1984 |
Titanium Round Bar Size Tolerances |
h11 |
Tolerance of Cold Rolled Titanium Round Bar Length |
Stock in special cut to length bar in tolerance – 0/+10mm (-0 +0.5 inch) |
Surface Finish of Cold Rolled Titanium Bar |
Cold drawn or Belt polished condition |
Bar Heat Treatment |
Annealed and Solution Annealed |
ASTM A276 Titanium Round Bar Grades
300 Series Titanium Grades |
Titanium 303, 304, 304L, 309, 310, 316, 316L, 316H, 317, 317L, 321, 347 |
400 Series Titanium Grades |
410, 410PSQ, 410QDT, 410HT, 416, 416HT, 416PSQ, 420 |
ASTM A276 Standard Titanium Rod Sizes
Type |
SIZES in milimeter |
SIZES in inches |
Tolerance |
Peeled and Polished |
40.00 - 150.00 |
1.50 - 6.00 |
h11, h11-DIN 1013 |
Cold Drawn and Polish |
3.00 to 75.00 |
1/8 to3.00 |
h8 to h11 |
Cold Drawn and Ground |
10.00 to 75.00 |
5/6 to 2.50 |
h8 to h11 |
Peeled nd Ground |
20.00 - 50.00 |
3/4 - 2.00 |
h9 to h11 |
ASTM A276 Titanium Round Bars Standard lengths of 2000 mm up to 6000 mm
5.0 |
45.0 |
6.0 |
50.0 |
7.0 |
55.0 |
8.0 |
60.0 |
9.0 |
65.0 |
10.0 |
70.0 |
12.0 |
75.0 |
16.0 |
80.0 |
20.0 |
90.0 |
25.0 |
100.0 |
30.0 |
130.0 |
35.0 |
160.0 |
40.0 |
200.0 |
ASTM A479 Titanium Round Bar Chemical Composition
ASTM Grade |
Carbon |
Manganese |
Silicon |
Sulfur |
Phospherous |
Chromium |
Nickel |
Molybdenum |
Other |
304 |
0.08 max |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
18.0-20.0 |
8.0 11.0 |
- |
- |
316 |
0.08 max |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
16.0-18.0 |
10.0 14.0 |
2.0 3.0 |
- |
317L |
0.035 max |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
18.0-20.0 |
11.0 14.0 |
3.0 4.0 |
- |
310 S |
0.08 max |
2.00 max |
1.5 max |
0.030 max |
0.045 max |
24.0-26.0 |
19.0 22.0 |
3.0 4.0 |
- |
347 H |
0.04 0.10 |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
17.0- 19.0 |
9.0 13.0 |
- |
10C(Cb+Ta)<1.10% |
321 |
0.08 |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
17.0-20.0 |
9.0 12.0 |
- |
5C 0.70% |
ASTM A276 Mechanical Properties of Forged Titanium Round Bar
Grade |
Elongation |
Density |
Tensile Strength |
Yield Strength (0.2%Offset) |
Melting Point |
Titanium 202 |
40 % |
8.0 g/cm3 |
515 MPa |
275 MPa |
1454 °C (2650 °F) |
Titanium 303 |
50 % |
55% |
Psi – 85,000 |
Psi – 45,000 |
Rb 180 |
Titanium 304 |
40% |
8.0 g/cm3 |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
1400 °C (2550 °F) |
Titanium 304L |
40% |
8.0 g/cm3 |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
1400 °C (2550 °F) |
Titanium 316 |
35 % |
8.0 g/cm3 |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
1454 °C (2650 °F) |
Titanium 316L |
40 % |
8.0 g/cm3 |
485 Min |
170 Min. |
1400 °C (2550 °F) |
ASTM A276 Round Titanium Bars Weight
Diameter(mm) |
Weight Chart(kg) |
Dia(in) |
Weight Chart(kg) |
3mm |
0.06 |
1/8" |
0.06 |
4mm |
0.10 |
3/16" |
0.14 |
5mm |
0.16 |
1/4" |
0.25 |
6mm |
0.22 |
5/16" |
0.39 |
7mm |
0.30 |
3/8" |
0.56 |
8mm |
0.40 |
7/16" |
0.77 |
10mm |
0.62 |
1/2" |
1.00 |
12mm |
0.89 |
9/16" |
1.22 |
14mm |
1.22 |
5/8" |
1.56 |
15mm |
1.40 |
11/16" |
1.89 |
16mm |
1.59 |
3/4" |
2.25 |
18mm |
2.01 |
7/8" |
3.07 |
20mm |
2.48 |
1" |
4.03 |
22mm |
3.00 |
|
|
24mm |
3.57 |
|
|
25mm |
3.88 |