ASTM A276 and ASTM A479 Tantalum Round Bar Weight, Dimensions Chart in mm, kg, PDF online
Tantalum round bars, also known as tantalum rods, are cylindrical metal bars made of tantalum. Tantalum
is a rare, dense, blue-gray metal that is highly resistant to corrosion. It has a high melting point and
is good conductor of heat and electricity. These properties make tantalum an ideal material for a wide
range of applications, including aerospace, chemical processing, electronics, and medical devices.
Tantalum round bars have many beneficial properties, which are useful in applications.These properties
are that they are highly corrosion resistant, have high melting point, good conductor of heat and
electricity, biocompatible and non-toxic, and are strong and durable. Different types of tantalum round
bars are hot-rolled round bars, cold-drawn round bars, and peeled and polished round bars. Tantalum
round bars come in a variety of sizes and diameters to suit different applications. Tantalum round bars
are manufactured according to various international standards and specifications to ensure quality and
compatibility with the intended application. Common standards include ASTM A276 and ASTM A479. Refer to
weight and dimensions chart PDF for tantalum round bar in mm, kg given below.
Tantalum round bar is a versatile material that can be used in a wide range of applications:
- Semiconductor manufacturing
- Laboratory benches and equipment
- Medical devices
- Heated exchangers
- Chemical containers, including for transport
- Aerospace applications
- Jet turbines
- Capacitors
Tantalum Bar Specifications
Tantalum Bar Length |
2 to 6 meters or 8 to 20 feet |
Tantalum Rod Chamfering |
Available in 30, 45 & 60 degree thru fully automatic both-end chamfering machine
|
Ultrasonic Test of ASTM A276 Threaded Rod |
As per ASTM A-388, EN 10308 (class 1 to 4), API 6A/ISO it is 100% tested thru Digital
Ultrasonic Flaw Detector, 10423:2003-PSL 3, MIL STD 2154, SEP 1920:1984 |
Tantalum Round Bar Size Tolerances |
h11 |
Tolerance of Cold Rolled Tantalum Round Bar Length |
Stock in special cut to length bar in tolerance – 0/+10mm (-0 +0.5 inch) |
Surface Finish of Cold Rolled Tantalum Bar |
Cold drawn or Belt polished condition |
Bar Heat Treatment |
Annealed and Solution Annealed |
ASTM A276 Tantalum Round Bar Grades
300 Series Tantalum Grades |
Tantalum 303, 304, 304L, 309, 310, 316, 316L, 316H, 317, 317L, 321, 347 |
400 Series Tantalum Grades |
410, 410PSQ, 410QDT, 410HT, 416, 416HT, 416PSQ, 420 |
ASTM A276 Standard Tantalum Rod Sizes
Type |
SIZES in milimeter |
SIZES in inches |
Tolerance |
Peeled and Polished |
40.00 - 150.00 |
1.50 - 6.00 |
h11, h11-DIN 1013 |
Cold Drawn and Polish |
3.00 to 75.00 |
1/8 to3.00 |
h8 to h11 |
Cold Drawn and Ground |
10.00 to 75.00 |
5/6 to 2.50 |
h8 to h11 |
Peeled nd Ground |
20.00 - 50.00 |
3/4 - 2.00 |
h9 to h11 |
ASTM A276 Tantalum Round Bars Standard lengths of 2000 mm up to 6000 mm
5.0 |
45.0 |
6.0 |
50.0 |
7.0 |
55.0 |
8.0 |
60.0 |
9.0 |
65.0 |
10.0 |
70.0 |
12.0 |
75.0 |
16.0 |
80.0 |
20.0 |
90.0 |
25.0 |
100.0 |
30.0 |
130.0 |
35.0 |
160.0 |
40.0 |
200.0 |
ASTM A479 Tantalum Round Bar Chemical Composition
ASTM Grade |
Carbon |
Manganese |
Silicon |
Sulfur |
Phospherous |
Chromium |
Nickel |
Molybdenum |
Other |
304 |
0.08 max |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
18.0-20.0 |
8.0 11.0 |
- |
- |
316 |
0.08 max |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
16.0-18.0 |
10.0 14.0 |
2.0 3.0 |
- |
317L |
0.035 max |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
18.0-20.0 |
11.0 14.0 |
3.0 4.0 |
- |
310 S |
0.08 max |
2.00 max |
1.5 max |
0.030 max |
0.045 max |
24.0-26.0 |
19.0 22.0 |
3.0 4.0 |
- |
347 H |
0.04 0.10 |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
17.0- 19.0 |
9.0 13.0 |
- |
10C(Cb+Ta)<1.10% |
321 |
0.08 |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
17.0-20.0 |
9.0 12.0 |
- |
5C 0.70% |
ASTM A276 Mechanical Properties of Forged Tantalum Round Bar
Grade |
Elongation |
Density |
Tensile Strength |
Yield Strength (0.2%Offset) |
Melting Point |
Tantalum 202 |
40 % |
8.0 g/cm3 |
515 MPa |
275 MPa |
1454 °C (2650 °F) |
Tantalum 303 |
50 % |
55% |
Psi – 85,000 |
Psi – 45,000 |
Rb 180 |
Tantalum 304 |
40% |
8.0 g/cm3 |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
1400 °C (2550 °F) |
Tantalum 304L |
40% |
8.0 g/cm3 |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
1400 °C (2550 °F) |
Tantalum 316 |
35 % |
8.0 g/cm3 |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
1454 °C (2650 °F) |
Tantalum 316L |
40 % |
8.0 g/cm3 |
485 Min |
170 Min. |
1400 °C (2550 °F) |
ASTM A276 Round Tantalum Bars Weight
Diameter(mm) |
Weight Chart(kg) |
Dia(in) |
Weight Chart(kg) |
3mm |
0.06 |
1/8" |
0.06 |
4mm |
0.10 |
3/16" |
0.14 |
5mm |
0.16 |
1/4" |
0.25 |
6mm |
0.22 |
5/16" |
0.39 |
7mm |
0.30 |
3/8" |
0.56 |
8mm |
0.40 |
7/16" |
0.77 |
10mm |
0.62 |
1/2" |
1.00 |
12mm |
0.89 |
9/16" |
1.22 |
14mm |
1.22 |
5/8" |
1.56 |
15mm |
1.40 |
11/16" |
1.89 |
16mm |
1.59 |
3/4" |
2.25 |
18mm |
2.01 |
7/8" |
3.07 |
20mm |
2.48 |
1" |
4.03 |
22mm |
3.00 |
|
|
24mm |
3.57 |
|
|
25mm |
3.88 |