Steel metal alloys have largely dominated many industries because of their excellent mechanical properties including strength, durability and corrosion resistance. Strip, plate and coil forming of steel alloy are widely used in construction, manufacturing and engineering applications. Mechanical, weight, dimension, size, and physical properties of building materials are remarkable in the designer's choice of this material for different projects. Our website has a comprehensive PDF that charts and a detailed table of actual data on mechanical, weight, dimension, size, and physical properties of the various steel alloy grades in sheet, plate and coil form. Regardless of whether you are an expert in the engineering field, a contractor, or a student, our resources will guide you throughout the process of the material selection, the best design, and implementation. Since dependable information is now easily accessible, you can efficiently run your operations, set up a system that works, and reach desired targets in the project.
| THICKNESS IN MM | SIZE IN MM | WEIGHT KG/M2 | ||
|---|---|---|---|---|
| 2000 X 1000 | 2500 X 1250 | 3000 X 1500 | ||
| 0.18 | 2.88 kg | - | - | 1.44 kg |
| 0.20 | 3.20 kg | - | - | 1.60 kg |
| 0.22 | 3.52 kg | - | - | 1.76 kg |
| 0.24 | 3.84 kg | - | - | 1.92 kg |
| 0.27 | 4.32 kg | - | - | 2.16 kg |
| 0.28 | 4.48 kg | - | - | 2.24 kg |
| 0.32 | 5.12 kg | - | - | 2.56 kg |
| 0.38 | 6.08 kg | - | - | 3.04 kg |
| 0.44 | 7.04 kg | 11.00 kg | - | 3.52 kg |
| 0.50 | 8.00 kg | 12.50 kg | - | 4.00 kg |
| 0.56 | 8.96 kg | 14.00 kg | - | 4.48 kg |
| 0.63 | 10.08 kg | 15.75 kg | - | 5.04 kg |
| 0.75 | 12.00 kg | 18.75 kg | - | 6.00 kg |
| 0.88 | 14.08 kg | 22.00 kg | - | 7.04 kg |
| 1.00 | 16.00 kg | 25.00 kg | 36.00 kg | 8.00 kg |
| .1.13 | 18.08 kg | 28.25 kg | 40.00 kg | 9.04 kg |
| 1.25 | 20.00 kg | 31.25 kg | 45.00 kg | 10.00 kg |
| 1.38 | 22.03 kg | 34.50 kg | 50.00 kg | 72.00 kg |
| 1.50 | 24.00 kg | 37.50 kg | 54.00 kg | 12.00 kg |
| 1.75 | 28.00 kg | 43.75 kg | 63.00 kg | 14.00 kg |
| 2.00 | 32.00 kg | 50.00 kg | 72.00 kg | 16.00 kg |
| 2.25 | 36 kg | 56.25 kg | 81 kg | 18 kg |
| 2.5 | 40 kg | 62.5 kg | 90 kg | 20 kg |
| 2.75 | 44 kg | 68.75 kg | 99 kg | 22 kg |
| 3 | 48 kg | 75 kg | 108 kg | 24 kg |
| 3.25 | 52 kg | 81.25 kg | 117 kg | 26 kg |
| 3.5 | 56 kg | 87.5 kg | 126 kg | 28 kg |
| 3.75 | 60 kg | 93.75 kg | 135 kg | 30 kg |
| 4 | 64 kg | 100 kg | 144 kg | 32 kg |
| 4.25 | 68 kg | 106.25 kg | 153 kg | 34 kg |
| 4.5 | 72 kg | 112.5 kg | 162 kg | 36 kg |
| 5 | 80 kg | 125 kg | 180 kg | 40 kg |
| 5.5 | 88 kg | 137.5 kg | 198 kg | 44 kg |
| 6 | 96 kg | 150 kg | 216 kg | 48 kg |
| 6.5 | 104 kg | 162.5 kg | 234 kg | 52 kg |
| 7 | 112 kg | 175 kg | 252 kg | 56 kg |
| 7.5 | 120 kg | 187.5 kg | 270 kg | 60 kg |
| 8 | 128 kg | 200 kg | 288 kg | 64 kg |
| Physical Properties | Metric | Comments |
|---|---|---|
| Density | 0.190 - 9.01 g/cc | Average value: 7.79 g/cc Grade Count:1432 |
| Porosity | 0.000 - 5.00 % | Average value: 2.97 % Grade Count:15 |
| Particle Size | 0.000 - 300 µm | Average value: 37.9 µm Grade Count:88 |
| Permeability | 0.0150 - 1.00 | Average value: 0.509 Grade Count:4 |
| Thickness | 20.0 - 508 microns | Average value: 86.8 microns Grade Count:14 |
| Mechanical Properties | Metric | Comments |
| Hardness, Brinell | 80.0 - 600 | Average value: 251 Grade Count:564 |
| Hardness, Knoop | 97.0 - 662 | Average value: 301 Grade Count:276 |
| Hardness, Rockwell A | 51.1 - 58.0 | Average value: 54.0 Grade Count:8 |
| Hardness, Rockwell B | 37.0 - 130 | Average value: 86.2 Grade Count:503 |
| Hardness, Rockwell C | 10.0 - 71.0 | Average value: 39.6 Grade Count:447 |
| Hardness, Vickers | 82.0 - 1100 | Average value: 294 Grade Count:339 |
| Tensile Strength, Ultimate | 32.3 - 3100 MPa | Average value: 935 MPa Grade Count:1729 |
| Tensile Strength, Yield | 25.0 - 2500 MPa | Average value: 669 MPa Grade Count:1638 |
| Elongation at Break | 0.000 - 88.0 % | Average value: 26.5 % Grade Count:1583 |
| Elongation at Yield | 0.000 - 62.0 % | Average value: 22.7 % Grade Count:22 |
| Reduction of Area | 0.500 - 88.0 % | Average value: 49.3 % Grade Count:308 |
| Modulus of Elasticity | 2.36 - 310 GPa | Average value: 196 GPa Grade Count:1175 |
| Flexural Yield Strength | 58.0 - 938 MPa | Average value: 479 MPa Grade Count:4 |
| Compressive Yield Strength | 262 - 3000 MPa | Average value: 1080 MPa Grade Count:11 |
| Notched Tensile Strength | 710 - 2230 MPa | Average value: 1740 MPa Grade Count:30 |
| Bulk Modulus | 166 GPa | Average value: 166 GPa Grade Count:14 |
| Poissons Ratio | 0.120 - 0.380 | Average value: 0.282 Grade Count:310 |
| Fatigue Strength | 85.0 - 1070 MPa | Average value: 439 MPa Grade Count:54 |
| Fracture Toughness | 17.6 - 165 MPa-m½ | Average value: 90.9 MPa-m½ Grade Count:9 |
| Machinability | 18.0 - 65.0 % | Average value: 31.7 % Grade Count:126 |
| Shear Modulus | 62.1 - 86.5 GPa | Average value: 77.6 GPa Grade Count:324 |
| Shear Strength | 74.5 - 597 MPa | Average value: 358 MPa Grade Count:5 |
| Izod Impact | 16.3 - 208 J | Average value: 115 J Grade Count:140 |
| Izod Impact Unnotched | 13.6 - 149 J | Average value: 77.8 J Grade Count:13 |
| Charpy Impact | 0.500 - 404 J | Average value: 115 J Grade Count:253 |
| Charpy Impact, Unnotched | 7.46 - 294 J | Average value: 157 J Grade Count:9 |
| Charpy Impact Unnotched | 1.59 - 60.0 J/cm² | Average value: 22.0 J/cm² Grade Count:3 |
| Charpy Impact, Notched | 0.710 - 294 J/cm² | Average value: 137 J/cm² Grade Count:5 |
| Taber Abrasion, mg/1000 Cycles | 3.20 - 30.0 | Average value: 11.3 Grade Count:3 |
| Electrical Properties | Metric | Comments |
| Electrical Resistivity | 0.00000450 - 0.000145 ohm-cm | Average value: 0.0000729 ohm-cm Grade Count:962 |
| Magnetic Permeability | 1.00 - 3000 | Average value: 178 Grade Count:316 |
| Magnetic Coercive Force, Hc | 1.20 - 7.00 Oe | Average value: 2.40 Oe Grade Count:6 |
| Magnetic Saturation Flux Density, Bmax | 11900 - 17000 Gauss | Average value: 15000 Gauss Grade Count:6 |
| Magnetic Remanence, Br | 2500 - 8500 Gauss | Average value: 6000 Gauss Grade Count:6 |
| Curie Temperature | -115 - 732 °C | Average value: 266 °C Grade Count:14 |
| Thermal Properties | Metric | Comments |
| CTE, linear | 7.02 - 21.1 µm/m-°C | Average value: 15.4 µm/m-°C Grade Count:977 |
| Specific Heat Capacity | 0.200 - 0.850 J/g-°C | Average value: 0.478 J/g-°C Grade Count:934 |
| Thermal Conductivity | 10.0 - 34.3 W/m-K | Average value: 16.7 W/m-K Grade Count:567 |
| Melting Point | 1230 - 1530 °C | Average value: 1440 °C Grade Count:580 |
| Solidus | 1230 - 1480 °C | Average value: 1410 °C Grade Count:553 |
| Liquidus | 1360 - 1530 °C | Average value: 1460 °C Grade Count:553 |
| Maximum Service Temperature, Air | 100 - 1400 °C | Average value: 837 °C Grade Count:368 |
| Minimum Service Temperature, Air | -200 - -30.0 °C | Average value: -133 °C Grade Count:26 |
| Optical Properties | Metric | Comments |
| Emissivity (0-1) | 0.7 | Average value: 0.700 Grade Count:4 |
| Processing Properties | Metric | Comments |
| Processing Temperature | 382 - 863 °C | Average value: 767 °C Grade Count:4 |
| Annealing Temperature | 593 - 1200 °C | Average value: 977 °C Grade Count:31 |
| Hot-Working Temperature | 482 - 1290 °C | Average value: 960 °C Grade Count:13 |
Our website contains a full guide about steel alloys, which includes mechanical properties, weight, dimensions, sizes, and physical properties, as well as a PDF guide or table that displays the information in a relevant table. Whether looking for material in sheet, plate, or coil forms, the data compiled by us will be no short of impactful for your selection process to be made easier. We offer an end-to-end resource that simplifies your investigation regarding the right steel alloy, and details on that aspect enable rational decision-making. Review the tensile strength and corrosion resistance among others among the steel grades. All the complex information you need for material selection will be available on a user-friendly and easy to navigate platform for you to use whenever you want. Rely on our website for correct, fresh information on steels alloy, which will simplify the ordering and application processes.