ASTM A276 and ASTM A479 Duplex Round Bar Weight, Dimensions Chart in mm, kg, PDF online
Duplex round bars are solid cylindrical bars made from duplex stainless steel, a type of stainless steel
known for its exceptional corrosion resistance, mechanical strength, and durability. Duplex round bars
are typically made from duplex stainless steel grades, with common grades being 2205 (UNS S32205/S31803)
and 2507 (UNS S32750). These grades typically consist of approximately 50% austenite and 50% ferrite
phases. Detailed information on these grades can be obtained in duplex round bar weight and dimensions
chart PDF.
Duplex round bars are corrosion-proof and rust-free, which makes them suitable for use in aggressive
environments. Duplex stainless steel has higher mechanical strength than conventional austenitic
stainless steels. This increased strength allows for the use of smaller-diameter round bars, reducing
weight and cost while maintaining structural integrity. This property is advantageous in various
high-stress applications. Duplex stainless steel round bars can be machined using standard machine
tools, but it's important to use appropriate cutting tools and techniques due to their higher strength
and work-hardening properties. Different types of duplex round bars are hot-rolled round bars,
cold-drawn round bars, and peeled and polished round bars. Duplex round bars come in a variety of sizes
and diameters to suit different applications. Duplex round bars are manufactured according to various
international standards and specifications to ensure quality and compatibility with the intended
application. Common standards include ASTM A276 and ASTM A479. Refer to weight and dimensions chart PDF
for duplex round bar in mm, kg given below.
Duplex round bars have some typical uses which include the following:
- Food and beverage processing equipment
- Pharmaceutical processing equipment
- Chemical processing equipment
- Nuclear power equipment
- Desalination equipment
- Marine engineering
- Water and wastewater treatment equipment
- General engineering applications
Duplex Bar Specifications
Duplex Bar Length |
2 to 6 meters or 8 to 20 feet |
Duplex Rod Chamfering |
Available in 30, 45 & 60 degree thru fully automatic both-end chamfering machine
|
Ultrasonic Test of ASTM A276 Threaded Rod |
As per ASTM A-388, EN 10308 (class 1 to 4), API 6A/ISO it is 100% tested thru Digital
Ultrasonic Flaw Detector, 10423:2003-PSL 3, MIL STD 2154, SEP 1920:1984 |
Duplex Round Bar Size Tolerances |
h11 |
Tolerance of Cold Rolled Duplex Round Bar Length |
Stock in special cut to length bar in tolerance – 0/+10mm (-0 +0.5 inch) |
Surface Finish of Cold Rolled Duplex Bar |
Cold drawn or Belt polished condition |
Bar Heat Treatment |
Annealed and Solution Annealed |
ASTM A276 Duplex Round Bar Grades
300 Series Duplex Grades |
Duplex 303, 304, 304L, 309, 310, 316, 316L, 316H, 317, 317L, 321, 347 |
400 Series Duplex Grades |
410, 410PSQ, 410QDT, 410HT, 416, 416HT, 416PSQ, 420 |
ASTM A276 Standard Duplex Rod Sizes
Type |
SIZES in milimeter |
SIZES in inches |
Tolerance |
Peeled and Polished |
40.00 - 150.00 |
1.50 - 6.00 |
h11, h11-DIN 1013 |
Cold Drawn and Polish |
3.00 to 75.00 |
1/8 to3.00 |
h8 to h11 |
Cold Drawn and Ground |
10.00 to 75.00 |
5/6 to 2.50 |
h8 to h11 |
Peeled and Ground |
20.00 - 50.00 |
3/4 - 2.00 |
h9 to h11 |
ASTM A276 Duplex Round Bars Standard lengths of 2000 mm up to 6000 mm
5.0 |
45.0 |
6.0 |
50.0 |
7.0 |
55.0 |
8.0 |
60.0 |
9.0 |
65.0 |
10.0 |
70.0 |
12.0 |
75.0 |
16.0 |
80.0 |
20.0 |
90.0 |
25.0 |
100.0 |
30.0 |
130.0 |
35.0 |
160.0 |
40.0 |
200.0 |
ASTM A479 Duplex Round Bar Chemical Composition
ASTM Grade |
Carbon |
Manganese |
Silicon |
Sulfur |
Phospherous |
Chromium |
Nickel |
Molybdenum |
Other |
304 |
0.08 max |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
18.0-20.0 |
8.0 11.0 |
- |
- |
316 |
0.08 max |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
16.0-18.0 |
10.0 14.0 |
2.0 3.0 |
- |
317L |
0.035 max |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
18.0-20.0 |
11.0 14.0 |
3.0 4.0 |
- |
310 S |
0.08 max |
2.00 max |
1.5 max |
0.030 max |
0.045 max |
24.0-26.0 |
19.0 22.0 |
3.0 4.0 |
- |
347 H |
0.04 0.10 |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
17.0- 19.0 |
9.0 13.0 |
- |
10C(Cb+Ta)<1.10% |
321 |
0.08 |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
17.0-20.0 |
9.0 12.0 |
- |
5C 0.70% |
ASTM A276 Mechanical Properties of Forged Duplex Round Bar
Grade |
Elongation |
Density |
Tensile Strength |
Yield Strength (0.2%Offset) |
Melting Point |
Duplex 202 |
40 % |
8.0 g/cm3 |
515 MPa |
275 MPa |
1454 °C (2650 °F) |
Duplex 303 |
50 % |
55% |
Psi – 85,000 |
Psi – 45,000 |
Rb 180 |
Duplex 304 |
40% |
8.0 g/cm3 |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
1400 °C (2550 °F) |
Duplex 304L |
40% |
8.0 g/cm3 |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
1400 °C (2550 °F) |
Duplex 316 |
35 % |
8.0 g/cm3 |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
1454 °C (2650 °F) |
Duplex 316L |
40 % |
8.0 g/cm3 |
485 Min |
170 Min. |
1400 °C (2550 °F) |
ASTM A276 Round Steel Bars Weight
Diameter(mm) |
Weight Chart(kg) |
Dia(in) |
Weight Chart(kg) |
3mm |
0.06 |
1/8" |
0.06 |
4mm |
0.10 |
3/16" |
0.14 |
5mm |
0.16 |
1/4" |
0.25 |
6mm |
0.22 |
5/16" |
0.39 |
7mm |
0.30 |
3/8" |
0.56 |
8mm |
0.40 |
7/16" |
0.77 |
10mm |
0.62 |
1/2" |
1.00 |
12mm |
0.89 |
9/16" |
1.22 |
14mm |
1.22 |
5/8" |
1.56 |
15mm |
1.40 |
11/16" |
1.89 |
16mm |
1.59 |
3/4" |
2.25 |
18mm |
2.01 |
7/8" |
3.07 |
20mm |
2.48 |
1" |
4.03 |
22mm |
3.00 |
|
|
24mm |
3.57 |
|
|
25mm |
3.88 |