ASTM A276 and ASTM A479 Nickel Alloy Round Bar Weight, Dimensions Chart in mm, kg, PDF online
Nickel alloy round bars are solid cylindrical bars made from various alloys of nickel. In these alloys,
nickel forms the main part along with other elements. These round bars are commonly made from
nickel-copper alloys (e.g., Monel), nickel-chromium-iron alloys (e.g., Inconel), and pure nickel. These
alloy consist of different percentages of elements mentioned above, different in each alloy. The choice
of alloy depends on the specific application and the required properties, such as corrosion resistance,
high-temperature strength, or low-temperature toughness. Detailed information on these alloys can be
obtained in nickel alloy round bar weight and dimensions chart PDF.
Nickel alloy round bars are corrosion-proof and rust-free, which makes them suitable for use in extreme
conditions. Nickel alloys has higher mechanical strength. This increased strength allows for the use of
smaller-diameter round bars, reducing weight and cost while preserving structural integrity. This
characteristic is advantageous in various high-stress applications. Nickel alloy round bars can be
machined using standard machine tools, but it's important to use appropriate cutting tools and
techniques due to their higher strength and durable properties. Different types of nickel alloy round
bars are Monel Round Bars (Alloy 400), Inconel Round Bars (e.g., Inconel 600, Inconel 625), Hastelloy
Round Bars (e.g., Hastelloy C276, Hastelloy C22), Nimonic Round Bars (e.g., Nimonic 75, Nimonic 90),
Incoloy Round Bars (e.g., Incoloy 800, Incoloy 825), Alloy 20 Round Bars(Carpenter 20), Nickel 200/201
Round Bars, Alloy 625 Round Bars and various other alloy round bars. Nickel alloy round bars come in a
variety of sizes and diameters to suit different applications. Nickel alloy round bars are manufactured
according to various international standards and specifications to ensure quality and compatibility with
the intended application. Common standards include ASTM A276 and ASTM A479. For knowing about these
standards and specifications in detail, refer to weight and dimensions chart given in mm and kg units,
below.
Nickel alloy round bars have some typical uses which include the following:
- Food and beverage processing equipment
- Pharmaceutical processing equipment
- Chemical processing equipment
- Nuclear power equipment
- Desalination equipment
- Marine engineering
- Water and wastewater treatment equipment
- General engineering applications
Nickel Alloy Bar Specifications
Nickel Alloy Bar Length |
2 to 6 meters or 8 to 20 feet |
Nickel Alloy Rod Chamfering |
Available in 30, 45 & 60 degree thru fully automatic both-end chamfering machine
|
Ultrasonic Test of ASTM A276 Threaded Rod |
As per ASTM A-388, EN 10308 (class 1 to 4), API 6A/ISO it is 100% tested thru Digital
Ultrasonic Flaw Detector, 10423:2003-PSL 3, MIL STD 2154, SEP 1920:1984 |
Nickel Alloy Round Bar Size Tolerances |
h11 |
Tolerance of Cold Rolled Nickel Alloy Round Bar Length |
Stock in special cut to length bar in tolerance – 0/+10mm (-0 +0.5 inch) |
Surface Finish of Cold Rolled Nickel Alloy Bar |
Cold drawn or Belt polished condition |
Bar Heat Treatment |
Annealed and Solution Annealed |
ASTM A276 Nickel Alloy Round Bar Grades
300 Series Nickel Alloy Grades |
Nickel Alloy 303, 304, 304L, 309, 310, 316, 316L, 316H, 317, 317L, 321, 347 |
400 Series Nickel Alloy Grades |
410, 410PSQ, 410QDT, 410HT, 416, 416HT, 416PSQ, 420 |
ASTM A276 Standard Nickel Alloy Rod Sizes
Type |
SIZES in milimeter |
SIZES in inches |
Tolerance |
Peeled and Polished |
40.00 - 150.00 |
1.50 - 6.00 |
h11, h11-DIN 1013 |
Cold Drawn and Polish |
3.00 to 75.00 |
1/8 to3.00 |
h8 to h11 |
Cold Drawn and Ground |
10.00 to 75.00 |
5/6 to 2.50 |
h8 to h11 |
Peeled and Ground |
20.00 - 50.00 |
3/4 - 2.00 |
h9 to h11 |
ASTM A276 Nickel Alloy Round Bars Standard lengths of 2000 mm up to 6000 mm
5.0 |
45.0 |
6.0 |
50.0 |
7.0 |
55.0 |
8.0 |
60.0 |
9.0 |
65.0 |
10.0 |
70.0 |
12.0 |
75.0 |
16.0 |
80.0 |
20.0 |
90.0 |
25.0 |
100.0 |
30.0 |
130.0 |
35.0 |
160.0 |
40.0 |
200.0 |
ASTM A479 Nickel Alloy Round Bar Chemical Composition
ASTM Grade |
Carbon |
Manganese |
Silicon |
Sulfur |
Phospherous |
Chromium |
Nickel |
Molybdenum |
Other |
304 |
0.08 max |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
18.0-20.0 |
8.0 11.0 |
- |
- |
316 |
0.08 max |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
16.0-18.0 |
10.0 14.0 |
2.0 3.0 |
- |
317L |
0.035 max |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
18.0-20.0 |
11.0 14.0 |
3.0 4.0 |
- |
310 S |
0.08 max |
2.00 max |
1.5 max |
0.030 max |
0.045 max |
24.0-26.0 |
19.0 22.0 |
3.0 4.0 |
- |
347 H |
0.04 0.10 |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
17.0- 19.0 |
9.0 13.0 |
- |
10C(Cb+Ta)<1.10% |
321 |
0.08 |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
17.0-20.0 |
9.0 12.0 |
- |
5C 0.70% |
ASTM A276 Mechanical Properties of Forged Nickel Alloy Round Bar
Grade |
Elongation |
Density |
Tensile Strength |
Yield Strength (0.2%Offset) |
Melting Point |
Nickel Alloy 202 |
40 % |
8.0 g/cm3 |
515 MPa |
275 MPa |
1454 °C (2650 °F) |
Nickel Alloy 303 |
50 % |
55% |
Psi – 85,000 |
Psi – 45,000 |
Rb 180 |
Nickel Alloy 304 |
40% |
8.0 g/cm3 |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
1400 °C (2550 °F) |
Nickel Alloy 304L |
40% |
8.0 g/cm3 |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
1400 °C (2550 °F) |
Nickel Alloy 316 |
35 % |
8.0 g/cm3 |
Psi – 75000 , MPa – 515 |
Psi – 30000 , MPa – 205 |
1454 °C (2650 °F) |
Nickel Alloy 316L |
40 % |
8.0 g/cm3 |
485 Min |
170 Min. |
1400 °C (2550 °F) |
ASTM A276 Round Nickel Alloy Bars Weight
Diameter(mm) |
Weight Chart(kg) |
Dia(in) |
Weight Chart(kg) |
3mm |
0.06 |
1/8" |
0.06 |
4mm |
0.10 |
3/16" |
0.14 |
5mm |
0.16 |
1/4" |
0.25 |
6mm |
0.22 |
5/16" |
0.39 |
7mm |
0.30 |
3/8" |
0.56 |
8mm |
0.40 |
7/16" |
0.77 |
10mm |
0.62 |
1/2" |
1.00 |
12mm |
0.89 |
9/16" |
1.22 |
14mm |
1.22 |
5/8" |
1.56 |
15mm |
1.40 |
11/16" |
1.89 |
16mm |
1.59 |
3/4" |
2.25 |
18mm |
2.01 |
7/8" |
3.07 |
20mm |
2.48 |
1" |
4.03 |
22mm |
3.00 |
|
|
24mm |
3.57 |
|
|
25mm |
3.88 |